ZG-P-5005/ZG-I-5002
1. Characteristics: Medium to high hardness,medium to high density PU resin for shoe sole. 2. Application: Applicable for the production of shoe sole with the upper for men and women.
Tel：+86-576-86992777
Email：yenina@hengtaiyuan.com
所属分类：
Big Bottom
Product description
Shop sign：ZG-P-5005/ZG-I-5002
1. Characteristics: Medium to high hardness,medium to high density PU resin for shoe sole
2. Application: Applicable for the production of shoe sole with the upper for men and women
| Name of products | Appearance |
Viscosity （Pa·s/50℃） |
Density （g/cm3/40℃） |
Package （kg） |
|
ZG-P-5005 |
White or pale yellow, liquid, no foreign material |
0.50-0.80 |
1.16-1.20 |
18 |
|
ZG-I-5002 |
Transparent liquid, no foreign material |
0.20-0.40 |
1.18-1.20 |
20 |
Reference shipments ratio: A/B=30/25(barrel)
ZG-P-5005/ZG-AC-2/水=18kg/260-300g/30-60
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratio P+C/I |
100/81-85 |
Molded density （g/cm3） |
0.42-0.55 |
|
Using temperature （℃） |
A material:40-45; B material:38-42 |
Hardness (type C) |
65-80 |
|
Cream time （s） |
5-9 |
Tensile strength （MPa） |
6.0-8.0 |
|
Rise time （s） |
30-45 |
Elongation （％） |
350-450 |
|
Metal mold temperature （℃） |
45-55 |
DIN abrasion resistance （g） |
＜400 |
|
Demould time Folding （min） |
2.5-4 |
Free foam density （g/cm3） |
0.24-0.30 |
|
Folding endurance (room temperature) (60,000 gap length mm) |
＜8 |
Shop sign:ZG-P-8009-4/ZG-I-5320
1. Characteristic: High hardness, high density shoes, good physical properties
2.Application: Suitable for the production of good rebound, excellent physical property of leisure sports shoes
| Name of products | Appearance |
Viscosity (Pa·s/50℃ ) |
Density (g/cm3/40℃ ) |
Package (kg) |
| ZG-P-8009-4 | White or pale yellow, liquid, no foreign material | 0.50-0.60 | 1. 16- 1.20 | 16.7 |
|
ZG-I-5320 |
Transparent liquid, no foreign material | 0. 10-0.30 | 1. 18- 1.20 | 20 |
Reference shipments ratio: A/B=30/24(barrel)
ZG-P-8009-4/ZG-AC-2/C-0607/Water/K-3 =18kg/150-200g/80-100g /90-110g/1.23Kg
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
| Reactivity | Technical index | Test item | Reference physical properties |
|
Reference ratio P+C/I |
100/80-85 |
Molded density (g/cm3 ) |
0.43-0.5 |
|
Using temperature (℃) |
A material:40-45; B material:40-45
|
Hardness (type C) |
55-65 |
|
Cream time ( s ) |
5-8 |
Tensile strength (MPa) |
4-6 |
|
Rise time ( s ) |
20-35 |
Elongation (％) |
350~450 |
|
Metal mold temperature (℃) |
45~55 |
DIN abrasion resistance (mm3) |
250-300 |
|
Demould time (min) |
3.5-4.5 |
Free foam density (g/cm3 ) |
0.21-0.25 |
|
Folding endurance(room temperature) (40,000 gap length mm) |
＜8 |
|
Shop sign: ZG-P-7800/ZG-I-9930-2
1. Characteristics: Low hardness,medium to low density and high-resilience PU resin for shoe sole
2. Application: Applicable for the production of Midsole and insole for men and women
|
Name of products |
Appearance |
Viscosity （Pa·s/50℃） |
Density （g/cm3/40℃） |
Package （kg） |
|
ZG-P-7800 |
White or pale yellow, liquid, no foreign material |
0.30-0.50 |
1.16-1.20 |
18 |
|
ZG-I-9930-2 |
Transparent liquid, no foreign material |
0.05-0.20 |
1.18-1.20 |
20 |
Reference shipments ratio: A/B=30/25(barrel)
ZG-P-7800/ZG-AC-2/water =18kg/260-300g/100-120
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratio P+C/I |
100/103-108 |
Molded density （g/cm3） |
0.28-0.35 |
|
Using temperature （℃） |
A material:40-45; B material:38-42 |
Hardness (type C) |
65-75 |
|
Cream time （s） |
3-5 |
Tensile strength （MPa） |
3.0-5.0 |
|
Rise time （s） |
25-35 |
Elongation （％） |
300-400 |
|
Metal mold temperature （℃） |
45-55 |
DIN abrasion resistance （g） |
------ |
|
Demould time Folding （min） |
2.5-3.5 |
Free foam density （g/cm3） |
0.14-0.18 |
|
Folding endurance(room temperature） (60,000 gap length mm) |
＜8 |
● Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
● Free foam density will vary with the seasons (temperature, humidity).
● Stripping time will be extended with the increase of the thickness of moldings.
● Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
● Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
Consult Now
If you are interested in our products, please leave your email address, and we will contact you as soon as possible. Thank you!
Contact Information
Zhejiang Factory：No. 1 Road, Science and Technology Park, Wenling Industrial Park, Zhejiang Province
Henan Factory： Intersection of Shahe Fifth Road and Chemical Industry First Road, Nylon City Industrial Cluster, Yexian County, Pingdingshan City, Henan Province
Mobile phone：+86-135 7588 6789
Email：yenina@hengtaiyuan.com
© 2024 Henan Hengtaiyuan New Materials Co., Ltd. Website supports ipv6